Casting High Leaded Tin Bronze C93900
Chemical Composition
| Element | |||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| Cu(1) | Pb | Sn | Zn | Fe | P(2) | Ni(3) | Al | S | Sb | Si | |
| (1) Cu + Sum of Named Elements 98.9% min.(2) For continuous castings P shall be 1.5% max.(3) Ni value includes Co. | |||||||||||
| Min (%) | 76.5 | 14.0 | 5.0 | ||||||||
| Max (%) | 79.5 | 18.0 | 7.0 | 1.5 | 0.40 | 1.5 | 0.8 | 0.005 | 0.08 | 0.50 | 0.005 |
Mechanical Properties*
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Brinell Hardness, 500 kg load | ||
|---|---|---|---|---|---|---|---|---|
| Not Applicable | NA | 32 Typ | 22 Typ | 7 | ||||
| As Continuous Cast | 25 Min for Standard 32 Typ |
16 Min for Standard 22 Typ |
5 Min for Standard 7 Typ |
63 Typ | ||||
| * Measured at room temperature, 68°F (20°C). | ||||||||
Physical Properties
| Melting Point - Liquidus°F | 1730 |
|---|---|
| Melting Point - Solidus°F | 1570 |
| Densitylb/cu in. at 68°F | 0.334 |
| Specific Gravity | 9.25 |
| Electrical Conductivity% IACS at 68°F | 11 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 30.2 |
| Coefficient of Thermal Expansion 68-39210-6 per °F (68 – 392°F) | 10.3 |
| Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tensionksi | 11000 |
| Incipient Melting°F | 600 |
| Magnetic Permeability | 1 |