C97300-Shanghai Unique Alloy Co. Ltd

Casting Leaded nickel bronze C97300

Chemical Composition

	Element
	Cu(1)	Pb	Sn	Zn	Fe	P	Ni(2)	Al	Mn	S	Sb	Si
(1) Cu + Sum of Named Elements 99.0% min.(2) Ni value includes Co.
Min (%)	53.0	8.0	1.5	17.0			11.0
Max (%)	58.0	11.0	3.0	25.0	1.5	0.05	14.0	0.005	0.50	0.08	0.35	0.15

Mechanical Properties*

Form	Temper	Temper Code	Tensile Strength (ksi)	YS-0.5% Ext (ksi)	Elongation (%)	Brinell Hardness, 500 kg load
As Centrifugal Cast	As Centrifugal Cast	M02	30 Min for Standard	15 Min for Standard	8 Min for Standard
As Continuous Cast	As Continuous Cast	M07	30 Min for Standard	15 Min for Standard	10 Min for Standard
As Sand Cast	As Sand Cast	M01	30 Min for Standard 35 Typ	15 Min for Standard 17 Typ	8 Min for Standard 20 Typ	55 Typ
* Measured at room temperature, 68°F (20°C).

Physical Properties

Melting Point - Liquidus°F	1904
Melting Point - Solidus°F	1850
Densitylb/cu in. at 68°F	0.321
Specific Gravity	8.89
Electrical Conductivity% IACS at 68°F	6
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F	16.5
Coefficient of Thermal Expansion 68-57210-6 per °F (68 – 572°F)	9
Specific Heat CapacityBtu/ lb /°F at 68°F	0.09
Modulus of Elasticity in Tensionksi	16000

Applicable Specifications

Form	Sub-Form	System	Standard	Description
As Centrifugal Cast	Castings	ASTM	B271/B271M	COPPER BASE ALLOY CENTRIFUGAL CASTINGS
As Continuous Cast	Castings	ASTM	B505/B505M	COPPER BASE ALLOY CONTINUOUS CASTINGS
	Castings	SAE	J461	WROUGHT AND CAST COPPER ALLOYS
	Castings	SAE	J462	CAST COPPER ALLOYS
As Sand Cast	Castings	ASTM	B584	COPPER ALLOY SAND CASTINGS FOR GENERAL APPLICATIONS
As Sand Cast	Castings	ASTM	B763/B763M	COPPER ALLOY SAND CASTINGS FOR VALVE APPLICATIONS
Ingot
Ingot		ASTM	B30	COPPER BASE ALLOYS IN INGOT FORM